- Wraparound repair cable large shrink wrap tubing with adhesive
- 【Brief 】：
Material: cross-linked polyolefin, inner coated with hot-melt adhesive
Standard color: black
Highlights: easy operation, wide range of selection, fit every occasion, excellent water repellency
Operating temperature:-40～+65℃
Shrink temperature:200℃
- 【Series】：Heat Shrink Cable Repair Sleeve
- Product description
CRS
Wraparound sleeve is mainly used for repairing outer/inner sheath/core damages on a HV cable and LV cable. It is made from cross-linked polyolefin which equals or exceeds the material properties of the original cable jacket. They can also be used for protecting against corrosion on metallic parts of the cable that are exposed to the outside.
Technical Data
Property
Test Method
Typical Data
Tensile strength
ASTM D2671
≥ 17MPa
Tensile strength after aging
ASTM D2671
≥ 14MPa
Elongation at break
ASTM D2671
≥ 350%
Elongation at break after aging
ASTM D2671/150℃, 168hrs
≥ 300%
Density
ASTM D792
0.94g/cm3
Longitudinal shrinkage
UL224
< 5%
Dielectric strength
IEC243
≥ 36kV/mm
Volume resistivity
IEC93
≥ 10 14 Ω · cm
Copper stability
ASTM D2671
Pass
Water absorptive
ISO 62/23℃, 14days
< 0.15%
Low Temperature Flexibility
ASTM D2671
No cracking
Resistance to fungus and decay
ISO 846
Pass
CRS heat shrink wraparound sleeve is closed with a flexible stainless-steel locking channel. Sleeve length is unlimited because of special production process. And the sleeve can be cut to suit short application requirements. Used for general re-jacketing and sealing applications, protection of damaged cable or repair of cable joints.